| PROPERTY |
HEC 010 + HEH 2000 |
HEC 010 + HEH 2001 |
HEC 010 + HEH 2002 |
HEC 010 + HEH 2003 |
| Mixture ratio in mass |
Each 100 g of
resin, 20 g of
hardener |
Each 100 g of
resin, 17 g of
hardener |
Each 100 g of
resin, 20 g of
hardener |
Each 100 g of
resin, 40 g of
hardener |
| Work time (25ºC, 100 ml, 40 mm) |
35 – 45 min |
15 – 25 min |
35 – 45 min |
160 – 190 min |
| Exothermic peak (100 ml, 40 mm, 25ºC) |
170 – 190 ºC |
120 – 140 ºC |
170 – 190 ºC |
45 – 55 ºC |
| Gel time (15 ml, 6 mm, 25ºC) |
90 – 120 min |
60 – 80 min |
90 – 120 min |
>5 min |
| Demolding (100 ml, 40 mm, 25ºC) |
8 – 10h |
5 – 10h |
8 – 10h |
8 – 10h |
| Post-cure (60ºC)¹ |
10 – 15h |
10 – 15h |
10 – 15h |
Approx. 48h |
| Recommended thickness |
5 mm |
5 mm |
5 mm |
5 mm |
¹Optional to achieve better mechanical properties
Check and, when required, homogenize the components before use. Add the correct quantity of hardener to the resin. Then, mix it well, preventing air bubbles from entering. Apply it right after using a brush, or manually, if it is in the form of a mass after adding the loads. Mineral or metallic loads can be added in the mixture. For the surface preparation (molds and models), see the bulletins related to the demolding agents (Z 15 LE or Z 25 LC).